LATEX

A. Latex non-sterile powdered gloves

The glove is using dusting powders as a lubricant for facilitating donning and to avoid sticking of the glove together. Latex non-sterile powdered gloves contains of 2 types that are examination and multipurpose gloves.

PRODUCT CHARACTERISTICS AND FEATURES FOR EXAMINATION AND MULTIPURPOSE GLOVES

  Material  Natural rubber latex
  Sterility    Non-Sterile
  Shape    Ambidextrous
  Color     Natural Color to White 
  Sizes      X-Small, Small, Medium, Large, X-Large
  Cuff Length (9”), beaded cuff
  Surface   Smooth finishing
  Lubricant Absorbable USP grade modified cornstarch powder
  Usage For single use only
  Mode of packing  100pieces per Inner box, 10 inner boxes per carton
  Shelf life  5 years from the date of manufacturer under recommended storage conditions
  Storage conditions Stored in a dry condition at temperature between 10°C to 30° C.  Direct sunlight should be avoided.

PERFORMANCE ATTRIBUTES FOR EXAMINATION AND MULTIPURPOSE GLOVES

(Sampling Plan – ISO 2859 Single Normal)
  Characteristics Inspection Level Acceptable Quality Level Reference Standard
Examination Multipurpose
  Freedom from holes – Barrier
   (1000 ml Water Leak Test)
GI 1.5 2.5 EN455-1-00
  Visual Defect   Major Visual GI 2.5 Industry Practice
  Minor Visual   4.0
  Dimensions S-2 4.0 ASTM D3578-10
  Physical Properties S-2 4.0 ASTM D3578-10
  Residual Powder Content N = 5 Less than 15 mg per glove ASTM D3578-10
ASTM D6124-11
  Protein Content N = 3 Less than 200 μg/gram of water-extractable protein ASTM D3578-10
ASTM D5712-10

PRODUCT PHYSICAL REQUIREMENTS FOR EXAMINATION AND MULTIPULPOSE GLOVES

  Dimensions
Physical Variable Size Specification Limits
  Length (mm) All sizes Min 240
  Average Palm Width (mm) XS
S
M
L
XL
70 ± 10
80 ± 10
95 ± 10
110 ± 10
120 ± 10
  Thickness (mm)
  *single wall
All sizes Finger   Min 0.12
Palm     Min 0.10
Cuff       Min 0.08

Physical Stress-Strain Properties

Properties Specification Limits
Before Aging After Aging
Examination Multipurpose Examination Multipurpose
  Elongation at break (%) – Average Min 650 Min 500
  Tensile Strength (MPa) – Average Min 18 Min 14
  Stress at 500% Elongation (MPa) Max 5.5 N/A
  Median Force at Break (N) Min 9 N/A Min 6 N/A

B. Latex non-sterile examination powder free

We are providing two types of powder free process that are with polymer coating for smooth donning and with chlorinated process with has an intensive washing process, thus the glove is lesser explosion from the risks associated with powdered and protein levels.

PRODUCT CHARACTERISTICS AND FEATURES FOR EXAMINATION GLOVES

  Material  Latex
  Sterility    Non-Sterile
  Shape    Ambidextrous
  Color     Natural Color / White 
  Sizes      X-Small, Small, Medium, Large, X-Large
  Cuff Length (9”), Beaded
  Glove Surface   Fully textured or smooth furnishing
  Lubricant Polymer coated and chlorinated
  Usage For single use only
  Mode of packing  100pieces per Inner box, 10 inner boxes per carton
  Shelf life  5 years from the date of manufacturer under recommended storage conditions
  Storage conditions Stored in a dry condition at temperature between 10°C to 30° C Direct sunlight should be avoided

PERFORMANCE ATTRIBUTES FOR POWDER FREE EXAMINATION POLYMER COATED AND CHLORINATED GLOVES

(Sampling Plan – ISO 2859 Single Normal)
  Characteristics Inspection Level Acceptable Quality Level Reference Standard
  Freedom from holes – Barrier
  (1000 ml Water Leak Test)
GI 1.5 EN455-1-00
  Visual Defect   Major Visual GI 2.5 Industry Practice
  Minor Visual 4.0
  Dimensions S-2 4.0 ASTM D3578-10
  Physical Properties S-2 4.0 ASTM D3578-10
  Residual Powder Content N = 5 Less than 2 mg per glove ASTM D3578-10
ASTM D6124-11
  Protein Content N = 3 Less than 50 μg/gram of water-extractable protein ASTM D3578-10
ASTM D5712-10

PRODUCT PHYSICAL REQUIREMENTS FOR POWDER FREE EXAMINATION POLYMER COATED AND CHLORINATED GLOVES

  Dimensions
Physical Variable Size Specification Limits
  Length (mm) All sizes Min 240
  Average Palm Width (mm) XS
S
M
L
XL
70 ± 10
80 ± 10
95 ± 10
110 ± 10
120 ± 10
  Thickness (mm)
  *single wall
All sizes Finger   Min 0.12
Palm     Min 0.10
Cuff       Min 0.08

Physical Stress-Strain Properties

Properties Specification Limits
Before Aging After Aging
  Elongation at break (%) – Average Min 650 Min 500
  Tensile Strength (MPa) – Average Min 18 Min 14
  Stress at 500% Elongation (MPa) Max 5.5 N/A
  Median Force at Break (N) Min 9 Min 6